Pulled Czochralski Ruby Rough

Laboratory created Czochralski Pulled Ruby,  each boule is about  35 mm in diameter. Material is very good quality,  pigeon blood color with true vitreous-adamantine luster of polished surface. This pigeon blood red is different from hydrothermal ruby, it's use different method to grown. Pulled method ruby can be used for big carats gems for faceting. 

Czochralski Process:

The Verneuil has some draw-backs for some ruby uses. It tends to produce crystals with high internal strain. Another method needed to be developed that could produce "whole boules" with less or no strain, especially for lazer rod use. The Czochralski process begins, like the Verneuil process with a movable seed crystal. Unlike the Verneuil process the crystal is located above a liquid melt and not below a flame.

The seed is placed on a moveable stage.The growth mixture is placed in an iridium crucible. For pure corundum, only pure aluminum oxide is used. To get the various colors, mixtures of aluminum oxide and the appropriate colorant(s) are premixed in the crucible. The iridium is used because its melting temperature is higher than that of the mixture. Iridium melts at 2442 C and the aluminum mixture melts around 2050 C.

A control system is used to maintain the temperature of the melt just a few degrees above the 2050 C of the alumia. In this case the atmosphere of the kiln is mostly nitrogen to keep the iridium crucible form oxidizing and reacting with the melt.

The seed crystal is lowered into the melt and just touches the top of the liquid. The melt goes into equilibrium with the seed crystals exterior and the seed is slowly withdrawn. If the temperature is too high, the seed melts and another must be added. If the temperature is too low, then the seed initiates the total crystallization of the melt. Temperature control is critical in this process.

As the seed crystal is withdrawn (and rotated- about 30 rpm) the newly formed crystal grows downward with the natural pull of gravity. The pull rate is about 25mm per hour. To create nearly perfect crystals the process is computer controlled using secondary measurements to maintain nearly perfect pulling speed and rotation. The secondary measurements may involve weighing the crucible during the process and continually calculating the weight loss of reactant. Or measuring spot temperatures near the crystal liquid contact point and adjusting the pull accordingly. 

Pulled czochralski ruby pigeon blood color wholesale price from China manufacturer

Czochralski method ruby rough
pulled ruby rough China manufacturer
Czochralski Pulled Ruby Raw Material
Czochralski method ruby rough pigeons blood
pigeons blood ruby rough China supplier
pigeons blood ruby rough wholesale
pigeons blood lab ruby
pigeons blood lab ruby wholesale China
pigeons blood ruby China supplier